Tabella acciai da bonifica - Caratteristiche chimiche e
meccaniche
Specifiche chimiche/meccaniche acciai da bonifica
Designaz.
(UNI EN 10083/1)
|
Composizione chimica
(analisi di colata) in % di massa
|
Re
(N/mm2)
(1)(3)
|
Rm
(N/mm2)
(1)(4)
|
KV
(J)
(1)(5)
|
C
|
Si
max |
Mn |
P
max |
S
|
Cr |
Mo
|
Ni
|
|
0.17÷0.24 |
0.40 |
0.40÷0.70 |
0.035 |
|
max 0.40 |
max 0.10 |
max 0.40 |
290 |
470÷620 |
50 |
|
0.22÷0.29 |
0.40 |
0.40÷0.70 |
0.035 |
|
max 0.40 |
max 0.10 |
max 0.40 |
320 |
500÷650 |
45 |
|
0.27÷0.34 |
0.40 |
0.50÷0.80 |
0.035 |
|
max 0.40 |
max 0.10 |
max 0.40 |
350 |
550÷700 |
40 |
|
0.32÷0.39 |
0.40 |
0.50÷0.80 |
0.035 |
|
max 0.40 |
max 0.10 |
max 0.40 |
380 |
600÷750 |
35 |
|
0.37÷0.44 |
0.40 |
0.50÷0.80 |
0.035 |
|
max 0.40 |
max 0.10 |
max 0.40 |
400 |
630÷780 |
30 |
|
0.42÷0.50 |
0.40 |
0.50÷0.80 |
0.035 |
|
max 0.40 |
max 0.10 |
max 0.40 |
430 |
650÷800 |
25 |
|
0.47÷0.55 |
0.40 |
0.60÷0.90 |
0.035 |
|
max 0.40 |
max 0.10 |
max 0.40 |
460 |
700÷850 |
- |
|
0.52÷0.60 |
0.40 |
0.60÷0.90 |
0.035 |
|
max 0.40 |
max 0.10 |
max 0.40 |
490 |
750÷900 |
- |
|
0.57÷0.65 |
0.40 |
0.60÷0.90 |
0.035 |
|
max 0.40 |
max 0.10 |
max 0.40 |
520 |
800÷960 |
- |
28 Mn 6
|
0.25÷032 |
0.40 |
1.30÷1.65 |
0.035 |
max 0.035 |
max 0.40 |
max 0.10 |
max 0.40 |
450 |
700÷850 |
40 |
|
0.35÷0.42 |
0.40 |
0.50÷0.80 |
0.035 |
|
0.40÷0.60 |
- |
- |
450 |
700÷850 |
35 |
|
0.42÷0.50 |
0.40 |
0.50÷0.80 |
0.035 |
|
0.40÷0.60 |
- |
- |
550 |
800÷950 |
35 |
|
0.30÷0.37 |
0.40 |
0.60÷0.90 |
0.035 |
|
0.90÷1.20 |
- |
- |
590 |
800÷950 |
40 |
|
0.34÷0.41 |
0.40 |
0.60÷0.90 |
0.035 |
|
0.90÷1.20 |
- |
- |
630 |
850÷1000 |
35 |
|
0.38÷0.45 |
0.40 |
0.60÷0.90 |
0.035 |
|
0.90÷1.20 |
- |
- |
660 |
900÷1100 |
35 |
|
0.22÷0.29 |
0.40 |
0.60÷0.90 |
0.035 |
|
0.90÷1.20 |
0.15÷0.30 |
- |
600 |
800÷950 |
50 |
|
0.30÷0.37 |
0.40 |
0.60÷0.90 |
0.035 |
|
0.90÷1.20 |
0.15÷0.30 |
- |
650 |
900÷1100 |
40 |
|
0.38÷0.45 |
0.40 |
0.60÷0.90 |
0.035 |
|
0.90÷1.20 |
0.15÷0.30 |
- |
700 |
1000÷1200 |
35 |
50 CrMo 4 |
0.46÷0.54 |
0.40 |
0.50÷0.80 |
0.035 |
max 0.035 |
0.90÷1.20 |
0.15÷0.30 |
- |
780 |
1000÷1200 |
30 |
36
CrNiMo 4 |
0.32÷0.40 |
0.40 |
0.50÷0.80 |
0.035 |
max 0.035 |
0.90÷1.20 |
0.15÷0.30 |
0.90÷1.20 |
800 |
1000÷1200 |
40 |
34
CrNiMo 6 |
0.30÷0.38 |
0.40 |
0.50÷0.80 |
0.035 |
max 0.035 |
1.30÷1.70 |
0.15÷0.30 |
1.30÷1.70 |
900 |
1100÷1300 |
45 |
30
CrNiMo 8 |
0.26÷0.34 |
0.40 |
0.30÷0.60 |
0.035 |
max 0.035 |
1.80÷2.20 |
0.30÷0.50 |
1.80÷2.20 |
1050 |
1250÷1450 |
30 |
36
CrNiMo 16 |
0.32÷0.39 |
0.40 |
0.30÷0.60 |
0.030 |
max 0.025 |
1.60÷2.00 |
0.25÷0.45 |
3.60÷4.10 |
1050 |
1250÷1450 |
30 |
51 CrV 4
(2) |
0.47÷0.55 |
0.40 |
0.70÷1.10 |
0.035 |
max 0.035 |
0.90÷1.20 |
- |
- |
800 |
1000÷1200 |
30 |
Designaz.
(UNI EN 10083/2)
|
Composizione chimica
(analisi di colata) in % di massa
|
Re
(N/mm2)
(1)(3)
|
Rm
(N/mm2)
(1)(4)
|
KV
(J)
(1)(5)
|
C
|
Si
max |
Mn |
P
max |
S
max
|
Cr
max |
Mo
max |
Ni
max |
1 C 22
|
0.17÷0.24 |
0.40 |
0.40÷0.70 |
0.045 |
0.045 |
0.040 |
0.10 |
0.40 |
290 |
470÷620 |
50 |
1 C 25
|
0.22÷0.29 |
0.40 |
0.40÷0.70 |
0.045 |
0.045 |
0.040 |
0.10 |
0.40 |
320 |
500÷650 |
45 |
1 C 30
|
0.27÷0.34 |
0.40 |
0.50÷0.80 |
0.045 |
0.045 |
0.040 |
0.10 |
0.40 |
350 |
550÷700 |
40 |
1 C 35
|
0.32÷0.39 |
0.40 |
0.50÷0.80 |
0.045 |
0.045 |
0.040 |
0.10 |
0.40 |
380 |
600÷750 |
35 |
1 C 40
|
0.37÷0.44 |
0.40 |
0.50÷0.80 |
0.045 |
0.045 |
0.040 |
0.10 |
0.40 |
400 |
630÷780 |
30 |
1 C 45
|
0.42÷0.50 |
0.40 |
0.50÷0.80 |
0.045 |
0.045 |
0.040 |
0.10 |
0.40 |
430 |
650÷800 |
25 |
1 C 50
|
0.47÷0.55 |
0.40 |
0.60÷0.90 |
0.045 |
0.045 |
0.040 |
0.10 |
0.40 |
460 |
700÷850 |
- |
1 C 55
|
0.52÷0.60 |
0.40 |
0.60÷0.90 |
0.045 |
0.045 |
0.040 |
0.10 |
0.40 |
490 |
750÷900 |
- |
1 C 60
|
0.57÷0.65 |
0.40 |
0.60÷0.90 |
0.045 |
0.045 |
0.040 |
0.10 |
0.40 |
520 |
800÷950 |
- |
Note:
(1)I valori Re, Rm e Kv sono relativi allo
stato bonificato
e indicativi in quanto specifici per sezioni di riferimento. I valori
sopra fanno riferimento a diametro 16÷40mm oppure nel caso
di prodotti piani per spessori 8÷20mm.
(2)L'acciaio 51 CrV 4 ha anche V = 0.10÷0.25 %.
(3)R
e: carico unitario di snervamento superiore
ovvero, qualora non si manifesti un limite di snervamento marcato,
carico unitario di scostamento dalla proporzionalità allo
0.2% R
p0.2.
(4)R
m: resistenza a trazione.
(5) KV: resilienza per provette longitudinali ISO con intaglio a V
(media di 3 valori singoli; nessun valore singolo può essere
minore del 70% del valore medio minimo).